EN10088-2 X6CrNiTi18-10, also known as 1.4541, is a stainless steel grade that is widely used in various industries due to its excellent corrosion resistance and good mechanical properties. This article provides a detailed overview of the chemical composition, mechanical properties, heat treatment conditions, available size range, low-temperature impact testing, primary applications, and supply cases from TJC Steel Group.

Chemical Composition:

The chemical composition of X6CrNiTi18-10 is carefully balanced to provide the desired properties. The typical chemical composition is as follows:

· Carbon (C): ≤ 0.08%

· Silicon (Si): ≤ 1.00%

· Manganese (Mn): ≤ 2.00%

· Phosphorus (P): ≤ 0.045%

· Sulfur (S): ≤ 0.030%

· Chromium (Cr): 17.00% - 19.00%

· Nickel (Ni): 9.00% - 12.00%

· Titanium (Ti): ≥ 5 × %C - 0.70%

Mechanical Properties:

The mechanical properties of 1.4541 stainless steel plate are as follows:

· Tensile Strength: 500 - 700 MPa

· Yield Strength: ≥ 240 MPa

· Elongation: ≥ 40%

· Hardness: ≤ 220 HB

Heat Treatment Conditions:

The steel is generally supplied in the solution-annealed condition. However, it can be further heat-treated to enhance specific properties. Typical heat treatment conditions are:

· Solution Annealing: Heat to 1040°C - 1100°C, followed by rapid cooling in water or air.

· Stress Relieving: Heat to 700°C - 750°C, hold for 1 - 2 hours, and then cool slowly.

Available Size Range:

TJC Steel Group offers X6CrNiTi18-10 stainless steel plates in a wide range of sizes to meet the specific needs of our customers. The available size range is as follows:

· Thickness: 3mm - 120mm

· Width: 1000mm - 3000mm

· Length: 2000mm - 12000mm

Low-Temperature Impact Testing:

The steel grade is suitable for use at low temperatures, and TJC Steel Group can provide low-temperature impact testing to ensure the material meets the required specifications for your application.

Primary Applications:

Due to its excellent corrosion resistance and good mechanical properties, X6CrNiTi18-10 is widely used in the following applications:

· Chemical and Petrochemical Industry: Equipment and components that require resistance to corrosion.

· Food Processing Industry: Equipment and containers that come into contact with food.

· Medical Equipment: Instruments and devices that require high levels of cleanliness and corrosion resistance.

· Architectural Applications: Cladding, roofing, and façade elements.

Supply Cases from TJC Steel Group:

TJC Steel Group has supplied X6CrNiTi18-10 stainless steel plates to numerous clients across various industries. One notable supply case is the supply of 1.4541 plates for the construction of a chemical processing plant. The plates were used to fabricate heat exchangers and piping systems, which required high resistance to corrosion and excellent mechanical properties at elevated temperatures.

In conclusion, EN10088-2 X6CrNiTi18-10, or 1.4541, is a versatile stainless steel grade that offers excellent corrosion resistance and good mechanical properties. TJC Steel Group is a trusted supplier of this material, providing high-quality plates in various sizes and ensuring that the material meets the required specifications for your application.